Abstract :
It is of great interest to synthesize boron carbide nanomaterials and explore their novel properties. We reported the synthesis of belt-like Si-doped boron carbide nanomaterials at a low temperature of 1500 [degrees]C with no catalyst. The structures and formation mechanism were investigated. Broad photoluminescence spectra between 400 and 500 nm were observed under 380 nm light excitation. The mechanism of the blue shift of the as-received samples in comparison with the reported boron carbide nanostructured materials is discussed. Key words: boron carbide, nanobelts, microstructure, XPS, photoluminescence. La synthese de nanomateriaux a base de carbure de bore et l'exploration de leurs nouvelles proprietes revetent un grand interet. Nous decrivons la synthese de nanomateriaux a base de carbure de bore dope par le silicium formant des nanoceintures a temperature basse (1500 [degrees]C), sans catalyseur. Nous avons etudie la structure et le mecanisme de formation de ces nanomateriaux. Lorsque nous les avons soumis a l'excitation par une lumiere d'une longueur d'onde de 380 nm, nous avons observe de larges bandes dans les spectres de photoluminescence entre 400 et 500 nm. Nous avons etudie le mecanisme de deplacement vers le bleu des echantillons obtenus tels quels en les comparant a des materiaux nanostructures a base de carbure de bore decrits dans la litterature. [Traduit par la Redaction] Mots-cles : carbure de bore, nanoceintures, microstructure, XPS, photoluminescence.